High strength and high rigidity aluminum-based alloy and production method therefor

ABSTRACT

An aluminum-based alloy having the general formula Al 100  -(a+b)Q a  M b  (wherein Q is V, Mo, Fe, W, Nb, and/or Pd; M is Mn, Fe, Co, Ni, and/or Cu; and a and b, representing a composition ratio in atomic percentages, satisfy the relationships 1≦a≦8, 0&lt;b&lt;5, and 3≦a+b≦8) having a metallographic structure comprising a quasi-crystalline phase, wherein the difference in the atomic radii between Q and M exceeds 0.01 Å, and said alloy does not contain rare earths, possesses high strength and high rigidity. The aluminum-based alloy is useful as a structural material for aircraft, vehicles and ships, and for engine parts; as material for sashes, roofing materials, and exterior materials for use in construction; or as materials for use in marine equipment, nuclear reactors, and the like.

CROSS-REFERENCE TO RELATED APPLICATION

This application is a continuation-in-part of application Ser. No. 08/550,753 filed on Oct. 31, 1995, the subject matter of the above-mentioned application which is specifically incorporated by reference herein.

BACKGROUND OF THE INVENTION

1. Field of the Invention

The present invention relates to an aluminum-based alloy for use in a wide range of applications such as in a structural material for aircraft, vehicles, and ships, and for engine parts. In addition, the present invention may be employed in sashes, roofing materials, and exterior materials for use in construction, or as material for use in marine equipment, nuclear reactors, and the like.

2. Description of Related Art

As prior art aluminum-based alloys, alloys incorporating various components such as Al--Cu, Al--Si, Al--Mg, Al--Cu--Si, Al--Cu--Mg, and Al--Zn--Mg are known. In all of the aforementioned, superior anti-corrosive properties are obtained at a light weight, and thus the aforementioned alloys are being widely used as structural material for machines in vehicles, ships, and aircraft, in addition to being employed in sashes, roofing materials, exterior materials for use in construction, structural material for use in LNG tanks, and the like.

However, the prior art aluminum-based alloys generally exhibit disadvantages such as a low hardness and poor heat resistance when compared to material incorporating Fe. In addition, although some materials have incorporated elements such as Cu, Mg, and Zn for increased hardness, disadvantages remain such as low anti-corrosive properties.

On the other hand, recently, experiments have been conducted in which a fine metallographic structure of aluminum-based alloys is obtained by means of performing quick-quench solidification from a liquid-melt state, resulting in the production of superior mechanical strength and anti-corrosive properties.

In Japanese Patent Application, First Publication No. 1-275732, an aluminum-based alloy comprising a composition AlM₁ X with a special composition ratio (wherein M₁ represents an element such as V, Cr, Mn, Fe, Co, Ni, Cu, Zr and the like, and X represents a rare earth element such as La, Ce, Sm, and Nd, or an element such as Y, Nb, Ta, Mm (misch metal) and the like), and having an amorphous or a combined amorphous/fine crystalline structure, is disclosed.

This aluminum-based alloy can be utilized as material with a high hardness, high strength, high electrical resistance, anti-abrasion properties, or as soldering material. In addition, the disclosed aluminum-based alloy has a superior heat resistance, and may undergo extruding or press processing by utilizing the superplastic phenomenon observed near crystallization temperatures.

However, the aforementioned aluminum-based alloy is disadvantageous in that high costs result from the incorporation of large amounts of expensive rare earth elements and/or metal elements with a high activity such as Y. Namely, in addition to the aforementioned use of expensive raw materials, problems also arise such as increased consumption and labor costs due to the large scale of the manufacturing facilities required to treat materials with high activities. Furthermore, this aluminum-based alloy having the aforementioned composition tends to display insufficient resistance to oxidation and corrosion.

SUMMARY OF THE INVENTION

It is an object of the present invention to provide an aluminum-based alloy, possessing superior strength, rigidity, and anti-corrosive properties, which comprises a composition in which rare earth elements or high activity elements such as Y are not incorporated, thereby effectively reducing the cost, as well as, the activity described in the aforementioned.

In order to solve the aforementioned problems, the present invention provides a high strength and high rigidity aluminum-based alloy consisting essentially of a composition represented by the general formula Al₁₀₀₋(a+b) Q_(a) M_(b) (wherein Q is at least one metal element selected from the group consisting of V, Mo, Fe, W, Nb, and Pd; M is at least one metal element selected from the group consisting of Mn, Fe, Co, Ni, and Cu; and a and b, which represent a composition ratio in atomic percentages, satisfy the relationships 1≦a≦8, 0<b<5, and 3≦a+b≦8) having a metallographic structure comprising a quasi-crystalline phase, wherein the difference in the atomic radii between Q and M exceeds 0.01 Å, and said alloy does not contain rare earths.

According to the present invention, by adding a predetermined amount of V, Mo, Fe, W, Nb, and/or Pd to Al, the ability of the alloy to form a quasi-crystalline phase is improved, and the strength, hardness, and toughness of the alloy is also improved. Moreover, by adding a predetermined amount of Mn, Fe, Co, Ni, and/or Cu, the effects of quick-quenching are enhanced, the thermal stability of the overall metallographic structure is improved, and the strength and hardness of the resulting alloy are also increased. Fe has both quasi-crystalline phase forming effects and alloy strengthening effects.

The aluminum-based alloy according to the present invention is useful as materials with a high hardness, strength, and rigidity. Furthermore, this alloy also stands up well to bending, and thus possesses superior properties such as the ability to be mechanically processed.

Accordingly, the aluminum-based alloys according to the present invention can be used in a wide range of applications such as in the structural material for aircraft, vehicles, and ships, as well as for engine parts. In addition, the aluminum-based alloys of the present invention may be employed in sashes, roofing materials, and exterior materials for use in construction, or as materials for use in marine equipment, nuclear reactors, and the like.

BRIEF DESCRIPTION OF THE DRAWINGS

FIG. 1 shows a construction of an example of a single roll apparatus used at the time of manufacturing a tape of an alloy of the present invention following quick-quench solidification.

FIG. 2 shows the analysis result of the X-ray diffraction of an alloy having the composition of Al₉₄ V₄ Fe₂.

FIG. 3 shows the analysis result of the X-ray diffraction of an alloy having the composition of Al₉₅ Mo₃ Ni₂.

FIG. 4 shows the thermal properties of an alloy having the composition of Al₉₄ V₄ Ni₂.

FIG. 5 shows the thermal properties of an alloy having the composition of Al₉₄ V₄ Mn₂.

FIG. 6 shows the thermal properties of an alloy having the composition of Al₉₅ Nb₃ Co₂.

FIG. 7 shows the thermal properties of an alloy having the composition of Al₉₅ Mo₃ Ni₂.

FIG. 8 shows the thermal properties of an alloy having the composition of Al₉₇ Fe₃.

FIG. 9 shows the thermal properties of an alloy having the composition of Al₉₇ Fe₅ Co₃.

FIG. 10 shows the thermal properties of an alloy having the composition of Al₉₇ Fe₁ Ni₃.

DETAILED DESCRIPTION OF THE PREFERRED EMBODIMENTS

The preferred embodiment of the present invention provides a high strength and high rigidity aluminum-based alloy consisting essentially of a composition represented by the general formula Al₁₀₀₋(a+b) Q_(a) M_(b) (wherein Q is at least one metal element selected from the group consisting of V, Mo, Fe, W, Nb, and Pd; M is at least one metal element selected from the group consisting of Mn, Fe, Co, Ni, and Cu; and a and b, which represent a composition ratio in atomic percentages, satisfy the relationships 1≦a≦8, 0<b<5, and 3≦a+b≦8), comprising a quasi-crystalline phase in the alloy, wherein the difference in the atomic radii between Q and M exceeds 0.01 Å, and said alloy does not contain rare earths.

In the following, the reasons for limiting the composition ratio of each component in the alloy according to the present invention are explained.

The atomic percentage of Al (aluminum) is in the range of 92≦Al≦97, preferably in the range of 94≦Al≦97. An atomic percentage for Al of less than 92% results in embrittlement of the alloy. On the other hand, an atomic percentage for Al exceeding 97% results in reduction of the strength and hardness of the alloy.

The amount of at least one metal element selected from the group consisting of V (vanadium), Mo (molybdenum), Fe (iron), W (tungsten), Nb (niobium), and Pd (palladium) in atomic percentage is at least 1% and does not exceed 8%; preferably, the amount is at least 2% and does not exceed 8%; more preferably, the amount is at least 2% and does not exceed 6%. If the amount is less than 1%, a quasi-crystalline phase cannot be obtained, and the strength is markedly reduced. On the other hand, if the amount exceeds 10%, coarsening (the diameter of particles is 500 nm or more) of a quasi-crystalline phase occurs, and this results in remarkable embrittlement of the alloy and reduction of (rupture) strength of the alloy.

The amount of at least one metal element selected from the group consisting of Mn (manganese), Fe (iron), Co (cobalt), Ni (nickel), and Cu (copper) in atomic percentage is less than 5%; preferably, the amount is at least 1% and does not exceed 3%; more preferably, the amount is at least 1% and does not exceed 2%. If the amount is 5% or more, forming and coarsening (the diameter of particles is 500 nm or more) of intermetallic compounds occur, and these result in remarkable embrittlement and reduction of toughness of the alloy.

Furthermore, with the present invention, the difference in radii between the atom selected from the above-mentioned group Q and the atom selected from the above-mentioned group M must exceed 0.01 Å. According to the Metals Databook (Nippon Metals Society Edition, 1984, published by Maruzen K. K.), the radii of the atoms contained in groups Q and M are as follows, and the differences in atomic radii for each combination are as shown in Table 1.

Q: V=1.32 Å, Mo=1.36 Å, Fe=1.24 Å, W=1.37 Å, Nb=1.43 Å, Pd=1.37 Å

M: Mn=1.12 Å or 1.50 Å, Fe=1.24 Å, Ni=1.25 Å, Co=1.25 Å, Cu=1.28 Å

Table 1 shows the differences in radii between atoms selected from group Q and atoms selected from group M for all combinations, as calculated from the above-listed atomic radius values.

                  TABLE 1     ______________________________________     Units: Å     ELEMENT Mn           Fe     Co     Ni   Cu     ______________________________________     V       0.20 or 0.18 0.08   0.07   0.07 0.04     Nb      0.31 or 0.07 0.19   0.18   0.18 0.15     Mo      0.24 or 0.14 0.12   0.11   0.11 0.08     Pd      0.25 or 0.13 0.13   0.12   0.12 0.09     W       0.25 or 0.13 0.13   0.12   0.12 0.09     Fe      0.12 or 0.26 0      0.01   0.01 0.04     ______________________________________

Therefore, of the combinations of Q and M expressed by the above-given general formula, the three combinations of:

Q=Fe, M=Fe

Q=Fe, M=Co

Q=Fe, M=Ni are excluded from the scope of the present invention.

If the difference in radii of the atom selected from group Q and the atom selected from group M is not more than 0.01 Å, then they tend to form thermodynamically stable intermetallic compounds which are undesirable for tending to become brittle upon solidification. For example, when forming bulk-shaped samples by solidifying ultra-quick-quenching tape, the intermetallic compounds leave prominent deposits so as to make the samples extremely brittle.

The formation of thermodynamically stable intermetallic compounds can be detected, for example, as decreases in the crystallization temperature by means of differential scanning calorimetry (DSC).

Additionally, brittleness can appear as reductions in the Charpy impact values.

Furthermore, the total amount of unavoidable impurities, such as Fe, Si, Cu, Zn, Ti, O, C, or N, does not exceed 0.3% by weight; preferably, the amount does not exceed 0.15% by weight; and more preferably, the amount does not exceed 0.10% by weight. If the amount exceeds 0.3% by weight, the effects of quick-quenching is lowered, and this results in reduction of the formability of a quasi-crystalline phase. Among the unavoidable impurities, particularly, it is preferable that the amount of O does not exceed 0.1% by weight and that the amount of C or N does not exceed 0.03% by weight.

The aforementioned aluminum-based alloys can be manufactured by quick-quench solidification of the alloy liquid-melts having the aforementioned compositions using a liquid quick-quenching method. This liquid quick-quenching method essentially entails rapid cooling of the melted alloy. For example, single roll, double roll, and submerged rotational spin methods have proved to be particularly effective. In these aforementioned methods, a cooling rate of 10⁴ to 10⁶ K/sec is easily obtainable.

In order to manufacture a thin tape using the aforementioned single or double roll methods, the liquid-melt is first poured into a storage vessel such as a silica tube, and is then discharged, via a nozzle aperture at the tip of the silica tube, towards a copper or copper alloy roll of diameter 30 to 300 mm, which is rotating at a fixed velocity in the range of 300 to 1000 rpm. In this manner, various types of thin tapes of thickness 5-500 μm and width 1-300 mm can be easily obtained.

On the other hand, fine wire-thin material can be easily obtained through the submerged rotational spin method by discharging the liquid-melt via the nozzle aperture, into a refrigerant solution layer of depth 1 to 10 cm, maintained by means of centrifugal force inside an air drum rotating at 50 to 500 rpm, under argon gas back pressure. In this case, the angle between the liquid-melt discharged from the nozzle, and the refrigerant surface is preferably 60 to 90 degrees, and the relative velocity ratio of the liquid-melt and the refrigerant surface is preferably 0.7 to 0.9.

In addition, thin layers of aluminum-based alloy of the aforementioned compositions can also be obtained without using the above methods, by employing layer formation processes such as the sputtering method. In addition, aluminum alloy powder of the aforementioned compositions can be obtained by quick-quenching the liquid-melt using various atomizer and spray methods such as a high pressure gas spray method.

In the following, examples of metallographic-structural states of the aluminum-based alloy obtained using the aforementioned methods are listed:

(1) Multiphase structure incorporating a quasi-crystalline phase and an aluminum phase;

(2) Multiphase structure incorporating a quasi-crystalline phase and a metal solid solution having an aluminum matrix;

(3) Multiphase structure incorporating a quasi-crystalline phase and a stable or metastable intermetallic compound phase; and

(4) Multiphase structure incorporating a quasi-crystalline phase, an amorphous phase, and a metal solid solution having am aluminum matrix.

The fine crystalline phase of the present invention represents a crystalline phase in which the crystal particles have an average maximum diameter of 1 μm.

By regulating the cooling rate of the alloy liquid-melt, any of the metallographic-structural states described in (1) to (4) above can be obtained.

The properties of the alloys possessing the aforementioned metallographic-structural states are described in the following.

An alloy of the multiphase structural state described in (1) and (2) above has a high strength and an excellent bending ductility.

An alloy of the multiphase structural state described in (3) above has a higher strength and lower ductility than the alloys of the multiphase structural state described in (1) and (2). However, the lower ductility does not hinder its high strength.

An alloy of the multiphase structural state described in (4) has a high strength, high toughness and a high ductility.

Each of the aforementioned metallographic-structural states can be easily determined by a normal X-ray diffraction method or by observation using a transmission electron microscope. In the case when a quasi-crystal exists, a dull peak, which is characteristic of a quasi-crystalline phase, is exhibited.

By regulating the cooling rate of the alloy liquid-melt, any of the multiphase structural states described in (1) to (3) above can be obtained.

By quick-quenching the alloy liquid-melt of the Al-rich composition (e.g., composition with Al≧92 atomic %), any of the metallographic-structural states described in (4) can be obtained.

The aluminum-based alloy of the present invention displays superplasticity at temperatures near the crystallization temperature (crystallization temperature ±50° C.), as well as, at the high temperatures within the fine crystalline stable temperature range, and thus processes such as extruding, pressing, and hot forging can easily be performed. Consequently, aluminum-based alloys of the above-mentioned compositions obtained in the aforementioned thin tape, wire, plate, and/or powder states can be easily formed into bulk materials by means of extruding, pressing and hot forging processes at the aforementioned temperatures. Furthermore, the aluminum-based alloys of the aforementioned compositions possess a high ductility, thus bending of 180° is also possible.

Additionally, the aforementioned aluminum-based alloys having multiphase structure composed of a pure-aluminum phase, a quasi-crystalline phase, a metal solid solution, and/or an amorphous phase, and the like, do not display structural or chemical non-uniformity of crystal grain boundary, segregation and the like, as seen in crystalline alloys. These alloys cause passivation due to formation of an aluminum oxide layer, and thus display a high resistance to corrosion. Furthermore, disadvantages exist when incorporating rare earth elements: due to the activity of these rare earth elements, non-uniformity occurs easily in the passive layer on the alloy surface resulting in the progress of corrosion from this portion towards the interior. However, since the alloys of the aforementioned compositions do not incorporate rare earth elements, these aforementioned problems are effectively circumvented.

In regards to the aluminum-based alloy of the aforementioned compositions, the manufacturing of bulk-shaped (mass) material will now be explained.

When heating the aluminum-based alloy according to the present invention, precipitation and crystallization of the fine crystalline phase is accompanied by precipitation of the aluminum matrix (α-phase), and when further heating beyond this temperature, the intermetallic compound also precipitates. Utilizing this property, bulk material possessing a high strength and ductility can be obtained.

Concretely, the tape alloy manufactured by means of the aforementioned quick-quenching process is pulverized in a ball mill, and then powder pressed in a vacuum hot press under vacuum (e.g. 10⁻³ Torr) at a temperature slightly below the crystallization temperature (e.g. approximately 470K), thereby forming a billet for use in extruding with a diameter and length of several centimeters. This billet is set inside a container of an extruder, and is maintained at a temperature slightly greater than the crystallization temperature for several tens of minutes. Extruded materials can then be obtained in desired shapes such as round bars, etc., by extruding.

EXAMPLES

(Hardness and Tensile Rupture Strength)

A molten alloy having a predetermined composition was manufactured using a high frequency melting furnace. Then, as shown in FIG. 1, this melt was poured into a silica tube 1 with a small aperture 5 (aperture diameter: 0.2 to 0.5 mm) at the tip, and then heated to melt, after which the aforementioned silica tube 1 was positioned directly above copper roll 2. This roll 2 was then rotated at a high speed of 4000 rpm, and argon gas pressure (0.7 kg/cm³) was applied to silica tube 1. Quick-quench solidification was subsequently performed by quick-quenching the liquid-melt by means of discharging the liquid-melt from small aperture 5 of silica tube 1 onto the surface of roll 2 and quick-quenching to yield an alloy tape 4.

Under these manufacturing conditions, the numerous alloy tape samples (width: 1 mm, thickness: 20 μm) of the compositions (atomic percentages) shown in Tables 2 and 3 were formed. The hardness (Hv) and tensile rupture strength (σ_(f) : MPa) of each alloy tape sample were measured. These results are also shown in Tables 2 and 3. The hardness is expressed in the value measured according to the minute Vickers hardness scale (DPN: Diamond Pyramid Number).

Additionally, a 180° contact bending test was conducted by bending each sample 180° and contacting the ends thereby forming a U-shape. The results of these tests are also shown in Tables 2 and 3: those samples which displayed ductility and did not rupture are designated Duc (ductile), while those which ruptured are designated Bri (brittle).

                  TABLE 2     ______________________________________     Sample Alloy composition                         of      Hv    Bending     No.    (at %)       (MPa)   (DPN) test     ______________________________________     1      Al.sub.95 V.sub.3 Ni.sub.2                          880    320   Duc   Example     2      Al.sub.94 V.sub.4 Ni.sub.2                         1230    365   Duc   Example     3      Al.sub.93 V.sub.5 Ni.sub.2                         1060    325   Duc   Example     4      Al.sub.95 V.sub.3 Fe.sub.2                          630    300   Duc   Example     5      Al.sub.94 V.sub.4 Fe.sub.2                         1350    370   Duc   Example     6      Al.sub.93 V.sub.5 Fe.sub.2                          790    305   Duc   Example     7      Al.sub.95 V.sub.3 Co.sub.2                          840    310   Duc   Example     8      Al.sub.94 V.sub.4 Co.sub.2                         1230    355   Duc   Example     9      Al.sub.93 V.sub.5 Co.sub.2                         1090    350   Duc   Example     10     Al.sub.94 V.sub.4 Mn.sub.2                         1210    355   Duc   Example     11     Al.sub.93 V.sub.4 Mn.sub.3                          800    310   Duc   Example     12     Al.sub.94 V.sub.4 Cu.sub.2                         1010    310   Duc   Example     14     Al.sub..sub.92 V.sub.5 Ni.sub.3                         1110    330   Duc   Example     15     Al.sub.93 V.sub.4 Fe.sub.3                         1200    340   Duc   Example     19     Al.sub.93 V.sub.6 Fe.sub.1                         1210    345   Duc   Example     17     Al.sub.92 V.sub.7 Co.sub.1                         1010    310   Duc   Example     18     Al.sub.93 V.sub.4 Co.sub.3                         1110    310   Duc   Example     19     Al.sub.94 Mo.sub.4 Ni.sub.2                         1200    300   Duc   Example     20     Al.sub.95 Mo.sub.3 Ni.sub.2                         1250    305   Duc   Example     21     Al.sub.93 Mo.sub.5 Ni.sub..sub.2                         1300    320   Duc   Example     22     Al.sub.94 Mo.sub.4 Co.sub.2                         1010    300   Duc   Example     23     Al.sub.95 Mo.sub.3 Co.sub.2                         1210    330   Duc   Example     24     Al.sub.93 Mo.sub.5 Fe.sub..sub.2                          990    310   Duc   Example     25     Al.sub.94 Mo.sub.4 Fe.sub.2                         1320    375   Duc   Example     26     Al.sub.94 Mo.sub.4 Mn.sub.2                         1220    360   Duc   Example     27     Al.sub.92 Mo.sub.5 Mn.sub.3                         1100    345   Duc   Example     28     Al.sub.95 Mo.sub.3 Mn.sub.2                         1020    330   Duc   Example     29     Al.sub.97 Mo.sub.1 Cu.sub.2                          880    305   Duc   Example     30     Al.sub.94 Fe.sub.4 Mn.sub.2                         1320    370   Duc   Exam     31     Al.sub.94 Fe.sub.3 Mn.sub.3                         1100    345   Duc   Exam     33     Al.sub.94 Fe.sub.4 Cu.sub.2                          890    285   Duc   Example     34     Al.sub.95 Fe.sub.4 Cu.sub.1                          880    300   Duc   Example     35     Al.sub.94 W.sub.4 Ni.sub..sub.2                         1010    340   Duc   Example     36     Al.sub.94 W.sub.3 Ni.sub.3                         1000    300   Duc   Example     37     Al.sub.93 W.sub.5 Co.sub.2                         1110    315   Duc   Example     38     Al.sub.95 W.sub.2 Co.sub.3                         1210    365   Duc   Example     39     Al.sub.94 W.sub.4 Fe.sub..sub.2                         1090    305   Duc   Example     40     Al.sub.93 W.sub.6 Fe.sub.1                         1100    360   Duc   Example     41     Al.sub.94 W.sub.2 Mn.sub.4                         1210    350   Duc   Example     42     Al.sub.92 Nb.sub.6 Mn.sub.2                         1230    330   Duc   Example     43     Al.sub.94 Nb.sub.4 Fe.sub.2                         1040    320   Duc   Example     44     Al.sub.94 Nb.sub.4 Ni.sub.2                         1300    370   Duc   Example     45     Al.sub.93 Nb.sub.3 Ni.sub.4                         1210    360   Duc   Example     46     Al.sub.95 Nb.sub.3 Ni.sub.2                         1100    360   Duc   Example     47     Al.sub.94 Nb.sub.4 Co.sub.2                         1150    365   Duc   Example     50     Al.sub.94 Pd.sub.4 Fe.sub.2                         1010    315   Duc   Example     51     Al.sub.96 Pd.sub.3 Fe.sub.1                          990    310   Duc   Example     52     Al.sub.94 Pd.sub.4 Ni.sub.2                         1210    365   Duc   Example     53     Al.sub.92 Pd.sub.5 Ni.sub.3                         1230    365   Duc   Example     54     Al.sub.94 Pd.sub.3 Co.sub.3                         1100    335   Duc   Example     ______________________________________

                  TABLE 3     ______________________________________     Sample           Alloy composition                        of      Hv    Bending     No    (at %)       (MPa)   (DPN) test     ______________________________________     55    Al.sub.94 Fe.sub.4 Co.sub.2                        1310    370   Duc   Comparative                                            Example     56    Al.sub.94 Fe.sub.5 Co.sub.1                        1110    335   Duc   Comparative                                            Example     57    Al.sub.96 Fe.sub.3 Co.sub.1                        1010    320   Duc   Comparative                                            Example     58    Al.sub.90 Fe.sub.8 Ni.sub.2                        1100    340   Duc   Comparative                                            Example     59    Al.sub.88 Fe.sub.10 Ni.sub.2                        1300    375   Duc   Comparative                                            Example     60    Al.sub.88 Fe.sub.9 Ni.sub.3                        1280    360   Duc   Comparative                                            Example     61    Al.sub.96.5 V.sub.0.5 Mn.sub.3                        460      95   Duc   Comparative                                            Example     62    Al.sub.86 V.sub.12 Mn.sub.2                        600     450   Bri   Comparative                                            Example     63    Al.sub.97 V.sub.3                        400     120   Duc   Comparative                                            Example     64    Al.sub.90 V.sub.4 Mn.sub.6                        550     410   Bri   Comparative                                            Example     65    Al.sub.98 V.sub.1 Mn.sub.1                        430      95   Duc   comparative                                            Example     66    Al.sub.87 V.sub.10 Mn.sub.3                        510     410   Bri   Comparative                                            Example     67    Al.sub.96.5 V.sub.0.5 Fe.sub.3                        410     120   Duc   Comparative                                            Example     68    Al.sub.85 V.sub.13 Fe.sub.2                        505     405   Bri   Comparative                                            Example     69    Al.sub.98 V.sub.1 Fe.sub.1                        400     110   Duc   Comparative                                            Example     70    Al.sub.87 V.sub.10 Fe.sub.3                        490     410   Bri   Comparative                                            Example     71    Al.sub.90 V.sub.4 Fe.sub.6                        450     430   Bri   Comparative                                            Example     72    Al.sub.95.5 V.sub.0.5 Ni.sub.4                        390      95   Duc   Comparative                                            Example     73    Al.sub.86 V.sub.11 Ni.sub.3                        410     430   Bri   Comparative                                            Example     74    Al.sub.89 V.sub.4 Ni.sub.7                        405     425   Bri   Comparative                                            Example     75    Al.sub.98 V.sub.1 Ni.sub.1                        290      80   Duc   Comparative                                            Example     76    Al.sub.85 V.sub.11 Ni.sub.4                        500     420   Bri   Comparative                                            Example     77    Al.sub.94.5 V.sub.0.5 Co.sub.5                        410     125   Duc   Comparative                                            Example     78    Al.sub.83 V.sub.15 Co.sub.2                        490     480   Bri   Comparative                                            Example     79    Al.sub.90 V.sub.2 Co.sub.8                        480     410   Bri   Comparative                                            Example     80    Al.sub.98.5 V.sub.0.5 Co.sub.1                        210      90   Duc   Comparative                                            Example     81    Al.sub.85 V.sub.11 Co.sub.4                        410     430   Bri   Comparative                                            Example     82    Al.sub.94.5 V.sub.0.5 Cu.sub.5                        340     105   Duc   Comparative                                            Example     83    Al.sub.88 V.sub.11 Cu.sub.1                        490     420   Bri   Comparative                                            Example     84    Al.sub.89 V.sub.3 Cu.sub.8                        480     410   Bri   Comparative                                            Example     85    Al.sub.98 V.sub.1 Cu.sub.1                        410      95   Duc   Comparative                                            Example     86    Al.sub.85 V.sub.12 Cu.sub.3                        550     420   Bri   Comparative                                            Example     87    Al.sub.96.5 Mo.sub.0.5 Mn.sub.3                        430     125   Duc   Comparative                                            Example     88    Al.sub.86 Mo.sub.12 Mn.sub.2                        510     430   Bri   Comparative                                            Example     89    Al.sub.97 Mo.sub.3                        370     130   Duc   Comparative                                            Example     90    Al.sub.90 Mo.sub.4 Mn.sub.6                        480     410   Bri   Comparative                                            Example     91    Al.sub.98 Mo.sub.1 Mn.sub.1                        380     100   Duc   Comparative                                            Example     92    Al.sub.87 Mo.sub.10 Mn.sub.3                        490     420   Bri   Comparative                                            Example     93    Al.sub.96.5 Mo.sub.0.5 Fe.sub.3                        360     125   Duc   Comparative                                            Example     94    Al.sub.85 Mo.sub.13 Fe.sub.2                        500     460   Bri   Comparative                                            Example     95    Al.sub.98 Mo.sub.1 Fe.sub.1                        210      80   Duc   Comparative                                            Example     96    Al.sub.87 Mo.sub.10 Fe.sub.3                        510     450   Bri   Comparative                                            Example     97    Al.sub.90 Mo.sub.4 Fe.sub.6                        490     435   Bri   Comparative                                            Example     98    Al.sub.95.5 Mo.sub.0.5 Ni.sub.4                        310      95   Duc   Comparative                                            Example     99    Al.sub.86 Mo.sub.11 Ni.sub.3                        500     430   Bri   Comparative                                            Example     100   Al.sub.89 Mo.sub.4 Ni.sub.7                        465     410   Bri   Comparative                                            Example     101   Al.sub.98 Mo.sub.1 Ni.sub.1                        200      95   Duc   Comparative                                            Example     102   Al.sub.85 Mo.sub.11 Ni.sub.4                        460     450   Bri   Comparative                                            Example     103   Al.sub.94 5 Mo.sub.0.5 Co.sub.5                        380     100   Duc   Comparative                                            Example     104   Al.sub.83 Mo.sub.15 Co.sub.2                        510     410   Bri   Comparative                                            Example     105   Al.sub.90 Mo.sub.2 Co.sub.8                        490     420   Bri   Comparative                                            Example     106   Al.sub.98.5 Mo.sub.0.5 Co.sub.1                        360     105   Duc   Comparative                                            Example     107   Al.sub.85 Mo.sub.11 Co.sub.4                        460     430   Bri   Comparative                                            Example     108   Al.sub.94.5 Mo.sub.0.5 Cu.sub.5                        340     105   Duc   Comparative                                            Example     109   Al.sub.88 Mo.sub.11 Cu.sub.1                        490     430   Bri   Comparative                                            Example     110   Al.sub.89 Mo.sub.3 Cu.sub.8                        510     410   Bri   Comparative                                            Example     111   Al.sub.98 Mo.sub.1 Cu.sub.1                        410      95   Duc   Comparative                                            Example     112   Al.sub.85 Mo.sub.12 Cu.sub.3                        550     420   Bri   Comparative                                            Example     113   Al.sub.96.5 Fe.sub.0.5 Mn.sub.3                        420     130   Duc   Comparative                                            Example     114   Al.sub.86 Fe.sub.12 Mn.sub.2                        510     430   Bri   Comparative                                            Example     115   Al.sub.97 Fe.sub.3                        480     160   Duc   Comparative                                            Example     116   Al.sub.90 Fe.sub.4 Mn.sub.6                        530     425   Bri   Comparative                                            Example     117   Al.sub.96 Fe.sub.1 Mn.sub.1                        480      95   Duc   Comparative                                            Example     118   Al.sub.87 Fe.sub.10 Mn.sub.3                        510     420   Bri   Comparative                                            Example     119   Al.sub.95.5 Fe.sub.0.5 Ni.sub.4                        470     105   Duc   Comparative                                            Example     120   Al.sub.86 Fe.sub.11 Ni.sub.3                        510     420   Bri   Comparative                                            Example     121   Al.sub.89 Fe.sub.4 Ni.sub.7                        505     425   Bri   Comparative                                            Example     122   Al.sub.98 Fe.sub.1 Ni.sub.1                        380      95   Duc   Comparative                                            Example     123   Al.sub.85 Fe.sub.11 Ni.sub.4                        500     410   Bri   Comparative                                            Example     124   Al.sub.94.5 Fe.sub.0.5 Co.sub.5                        380     125   Duc   Comparative                                            Example     125   Al.sub.83 Fe.sub.15 Co.sub.2                        200     480   Bri   Comparative                                            Example     126   Al.sub.90 Fe.sub.2 Co.sub.8                        490     425   Bri   Comparative                                            Example     127   Al.sub.98.5 Fe.sub.0.5 Co.sub.1                        380      95   Duc   Comparative                                            Example     128   Al.sub.85 Fe.sub.11 Co.sub.4                        350     435   Bri   Comparative                                            Example     129   Al.sub.94.5 Fe.sub.0.5 Cu.sub.5                        340     105   Duc   Comparative                                            Example     130   Al.sub.88 Fe.sub.11 Cu.sub.1                        410     435   Bri   Comparative                                            Example     131   Al.sub.89 Fe.sub.3 Cu.sub.8                        480     410   Bri   Comparative                                            Example     132   Al.sub.98 Fe.sub.1 Cu.sub.1                        410      95   Duc   Comparative                                            Example     133   Al.sub.85 Fe.sub.12 Cu.sub.3                        550     420   Bri   Comparative                                            Example     134   Al.sub.96.5 W.sub.0.5 Mn.sub.3                        380     120   Duc   Comparative                                            Example     135   Al.sub.86 W.sub.12 Mn.sub.2                        420     435   Bri   Comparative                                            Example     136   Al.sub.97 W.sub.3                        280      95   Duc   Comparative                                            Example     137   Al.sub.90 W.sub.4 Mn.sub.6                        490     440   Bri   Comparative                                            Example     138   Al.sub.98 W.sub.1 Mn.sub.1                        280      95   Duc   Comparative                                            Example     139   Al.sub.87 W.sub.10 Mn.sub.3                        290     475   Bri   Comparative                                            Example     140   Al.sub.96.5 W.sub.0.5 Fe.sub.3                        385     105   Duc   Comparative                                            Example     141   Al.sub.85 W.sub.13 Fe.sub.2                        310     480   Bri   Comparative                                            Example     142   Al.sub.98 W.sub.1 Fe.sub.1                        320     105   Duc   Comparative                                            Example     143   Al.sub.87 W.sub.10 Fe.sub.3                        500     475   Bri   Comparative                                            Example     144   Al.sub.90 W.sub.4 Fe.sub.6                        510     460   Bri   Comparative                                            Example     145   Al.sub.95.5 W.sub.0.5 Ni.sub.4                        380      95   Duc   Comparative                                            Example     146   Al.sub.86 W.sub.11 Ni.sub.13                        520     470   Bri   Comparative                                            Example     147   Al.sub.89 W.sub.4 Ni.sub.7                        500     435   Bri   Comparative                                            Example     148   Al.sub.98 W.sub.1 Ni.sub.1                        280      80   Duc   Comparative                                            Example     149   Al.sub.85 W.sub.11 Ni.sub.4                        460     435   Bri   Comparative                                            Example     150   Al.sub.94.5 W.sub.0.5 Co.sub.5                        275     105   Duc   Comparative                                            Example     151   Al.sub.83 W.sub.15 Co.sub.2                        500     460   Bri   Comparative                                            Example     152   Al.sub.90 W.sub.2 Co.sub.8                        410     445   Bri   Comparative                                            Example     153   Al.sub.98.5 W.sub.0.5 Co.sub.1                        270      85   Duc   Comparative                                            Example     154   Al.sub.85 W.sub.11 Co.sub.4                        290     470   Bri   Comparative                                            Example     155   Al.sub.94.5 W.sub.0.5 Cu.sub.5                        340     105   Duc   Comparative                                            Example     156   Al.sub.88 W.sub.11 Cu.sub.1                        310     435   Bri   Comparative                                            Example     157   Al.sub.89 W.sub.3 Cu.sub.8                        380     410   Bri   Comparative                                            Example     158   Al.sub.98 W.sub.1 Cu.sub.1                        410      95   Duc   Comparative                                            Example     159   Al.sub.85 W.sub.12 Cu.sub.3                        550     420   Bri   Comparative                                            Example     160   Al.sub.96.5 Nb.sub.0.5 Mn.sub.3                        430     120   Duc   Comparative                                            Example     161   Al.sub.86 Nb.sub.12 Mn.sub.2                        510     475   Bri   Comparative                                            Example     162   Al.sub.97 Nb.sub.3                        430     105   Duc   Comparative                                            Example     163   Al.sub.90 Nb.sub.4 Mn.sub.6                        490     430   Bri   Comparative                                            Example     164   Al.sub.98 Nb.sub.1 Mn.sub.1                        380      95   Duc   Comparative                                            Example     165   Al.sub.87 Nb.sub.10 Mn.sub.3                        390     465   Bri   Comparative                                            Example     166   Al.sub.96.5 Nb.sub.0.5 Fe.sub.3                        400      95   Duc   Comparative                                            Example     167   Al.sub.85 Nb.sub.13 Fe.sub.2                        390     480   Bri   Comparative                                            Example     168   Al.sub.98 Nb.sub.1 Fe.sub.1                        430     100   Duc   Comparative                                            Example     169   Al.sub.87 Nb.sub.10 Fe.sub.3                        510     435   Bri   Comparative                                            Example     170   Al.sub.90 Nb.sub.4 Fe.sub.6                        420      80   Bri   Comparative                                            Example     171   Al.sub.95.5 Nb.sub.0.5 Ni.sub.4                        380     110   Duc   Comparative                                            Example     172   Al.sub.86 Nb.sub.11 Ni.sub.3                        510     440   Bri   Comparative                                            Example     173   Al.sub.69 Nb.sub.4 Ni.sub.7                        490     435   Bri   Comparative                                            Example     174   Al.sub.98 Nb.sub.1 Ni.sub.1                        230      80   Duc   Comparative                                            Example     175   Al.sub.85 Nb.sub.11 Ni.sub.4                        430     475   Bri   Comparative                                            Example     176   Al.sub.94.5 Nb.sub.0.5 Co.sub.5                        280      95   Duc   Comparative                                            Example     177   Al.sub.83 Nb.sub.15 Co.sub.2                        410     470   Bri   Comparative                                            Example     178   Al.sub.90 Nb.sub.2 Co.sub.8                        510     430   Bri   Comparative                                            Example     179   Al.sub.98.5 Nb.sub.0.5 Co.sub.1                        270      90   Duc   Comparative                                            Example     180   Al.sub.85 Nb.sub.11 Co.sub.4                        510     475   Bri   Comparative                                            Example     181   Al.sub.94.5 Nb.sub.0.5 Cu.sub.5                        340     105   Duc   Comparative                                            Example     182   Al.sub.88 Nb.sub.11 Cu.sub.1                        490     445   Bri   Comparative                                            Example     183   Al.sub.89 Nb.sub.3 Cu.sub.8                        475     410   Bri   Comparative                                            Example     184   Al.sub.98 Nb.sub.1 Cu.sub.1                        410      95   Duc   Comparative                                            Example     185   Al.sub.85 Nb.sub.12 Cu.sub.3                        550     420   Bri   Comparative                                            Example     186   Al.sub.96.5 Pd.sub.0.5 Mn.sub.3                        380     105   Duc   Comparative                                            Example     187   Al.sub.86 Pd.sub.12 Mn.sub.2                        400     435   Bri   Comparative                                            Example     188   Al.sub.97 Pd.sub.3                        410      95   Duc   Comparative                                            Example     189   Al.sub.90 Pd.sub.4 Mn.sub.6                        510     420   Bri   Comparative                                            Example     190   Al.sub.98 Pd.sub.1 Mn.sub.1                        390      80   Duc   Comparative                                            Example     191   Al.sub.87 Pd.sub.10 Mn.sub.3                        490     465   Bri   Comparative                                            Example     192   Al.sub.96.5 Pd.sub.0.5 Fe.sub.3                        300      95   Duc   Comparative                                            Example     193   Al.sub.85 Pd.sub.13 Fe.sub.2                        210     480   Bri   Comparative                                            Example     194   Al.sub.98 Pd.sub.1 Fe.sub.1                        290     105   Duc   Comparative                                            Example     195   Al.sub.87 Pd.sub.10 Fe.sub.3                        460     435   Bri   Comparative                                            Example     196   Al.sub.90 Pd.sub.4 Fe.sub.6                        475     430   Bri   Comparative                                            Example     197   Al.sub.95.5 Pd.sub.0.5 Ni.sub.4                        310      90   Duc   Comparative                                            Example     198   Al.sub.86 Pd.sub.11 Ni.sub.3                        410     465   Bri   Comparative                                            Example     199   Al.sub.89 Pd.sub.4 Ni.sub.7                        460     450   Bri   Comparative                                            Example     200   Al.sub.96 Pd.sub.1 Ni.sub.1                        280      85   Duc   Comparative                                            Example     201   Al.sub.65 Pd.sub.11 Ni.sub.4                        410     460   Bri   Comparative                                            Example     202   Al.sub.94.5 Pd.sub.0.5 Co.sub.5                        430     120   Duc   Comparative                                            Example     203   Al.sub.83 Pd.sub.15 Co.sub.2                        290     485   Bri   Comparative                                            Example     204   Al.sub.90 Pd.sub.2 Co.sub.8                        425     430   Bri   Comparative                                            Example     205   Al.sub.98.5 Pd.sub.0.5 Co.sub.1                        290      95   Duc   Comparative                                            Example     206   Al.sub.85 Pd.sub.11 Co.sub.4                        460     465   Bri   Comparative                                            Example     207   Al.sub.94.5 Pd.sub.0.5 Cu.sub.5                        340     105   Duc   Comparative                                            Example     208   Al.sub.88 Pd.sub.11 Cu.sub.1                        475     435   Bri   Comparative                                            Example     209   Al.sub.89 Pd.sub.3 Cu.sub.8                        490     410   Bri   Comparative                                            Example     210   Al.sub.98 Pd.sub.1 Cu.sub.1                        410      95   Duc   Comparative                                            Example     211   Al.sub.85 Pd.sub.12 Cu.sub.3                        550     420   Bri   Comparative                                            Example     ______________________________________

It is clear from the results shown in Tables 2 and 3 that an aluminum-based alloy possessing a high bearing force and hardness, which endured bending and could undergo processing, was obtainable when the alloy comprising at least one of Mn, Fe, Co, Ni, and Cu, as element M, in addition to an Al--V, Al--Mo, Al--W, Al--Fe, Al--Nb, or Al--Pd two-component alloy has the atomic percentages satisfying the relationships Al_(balance) Q_(a) M_(b), 1≦a≦8, 0<b<5, 3≦a+b≦8, Q=V, Mo, Fe, W, Nb, and/or Pd, and M=Mn, Fe, Co, Ni, and/or Cu, wherein the difference in the atomic radii between Q and M exceeds 0.01 Å and the alloy does not contain rare-earths.

In contrast to normal aluminum-based alloys which possess an Hv of approximately 50 to 100 DPN, the samples according to the present invention, shown in Table 2, display an extremely high hardness from 295 to 375 DPN.

In addition, in regards to the tensile rupture strength (σ_(f)), normal age hardened type aluminum-based alloys (Al--Si--Fe type) possess values from 200 to 600 MPa; however, the samples according to the present invention have clearly superior values in the range from 630 to 1350 MPa.

Furthermore, when considering that the tensile strengths of aluminum-based alloys of the AA6000 series (alloy name according to the Aluminum Association (U.S.A.)) and AA7000 series which lie in the range from 250 to 300 MPa, Fe-type structural steel sheets which possess a value of approximately 400 MPa, and high tensile strength steel sheets of Fe-type which range from 800 to 980 MPa, it is clear that the aluminum-based alloys according to the present invention display superior values.

(X-ray Diffraction)

FIG. 2 shows an X-ray diffraction pattern possessed by an alloy sample having the composition of Al₉₄ V₄ Fe₂. FIG. 3 shows an X-ray diffraction pattern possessed by an alloy sample having the composition of Al₉₅ Mo₃ Ni₂. According to these patterns, each of these three alloy samples has a multiphase structure comprising a fine Al-crystalline phase having an fcc structure and a fine regular-icosahedral quasi-crystalline phase. In these patterns, peaks expressed as (111), (200), (220), and (311) are crystalline peaks of Al having an fcc structure, while peaks expressed as (211111) and (221001) are dull peaks of regular-icosahedral quasi crystals.

(Crystallization Temperature Measurement)

FIG. 4 shows the DSC (Differential Scanning Calorimetry) curve in the case when an alloy having the composition of Al₉₄ V₄ Ni₂ is heated at rate of 0.67 K/s, FIG. 5 shows the same for Al₉₄ V₄ Mn₂, FIG. 6 shows the same for Al₉₅ Nb₃ Co₂, and FIG. 7 shows the same for Al₉₅ Mo₃ Ni₂. In these figures, a dull exothermal peak, which is obtained when a quasi-crystalline phase is changed to a stable crystalline phase, is seen in the high temperature region exceeding 300° C.

FIG. 8 shows the DSC curve in the case when an alloy having the composition of Al₉₇ Fe₃ is heated at a rate of 0.67 K/s, FIG. 9 shows the same for Al₉₂ Fe₅ Co₃, and FIG. 10 shows the same for Al₉₆ Fe₁ Ni₃, each of which has an atomic radius difference between Q and M or 0.01 Å or less. In the DSC curves of these samples, the crystallization temperature which is indicated by the temperature at the starting end of the exothermal peak is each 300° C. or less, which is comparatively low in comparison to the results of FIGS. 4-7, thereby suggesting that thermodynamically stable intermetallic compounds are formed.

(Charpy Impact Values)

Alloy samples having the compositions indicated below were prepared, and their Charpy impact values were measured. That is, after preparing a rapidly hardened powder by means of high-pressure atomization, a powder having a grain size of 25 μm or less was separated out, filled into a copper container and formed into a billet, then bulk samples were made using a 100-ton warm press with a cross-sectional reduction rate of 80%, a push-out speed of 5 mm/s and a push-out temperature of 573K. Using these bulk samples, a Charpy impact test was performed. The results are shown in Table 4.

                  TABLE 4     ______________________________________                  Units: kgf-m/cm.sup.2     Composition  Charpy Impact Value     ______________________________________     Al.sub.94 V.sub.4 Mn.sub.2                  1.2     Al.sub.95 Nb.sub.3 Co.sub.2                  1.1     Al.sub.95 Mo.sub.3 Ni.sub.2                  1.2     Al.sub.95 W.sub.4 Cu.sub.1                  1.2     Al.sub.93 V.sub.5 Fe.sub.2                  1     Al.sub.95 Nb.sub.3 Cu.sub.2                  1.5     Al.sub.93 V.sub.4 Ni.sub.2                  1.2     Al.sub.93 Mo.sub.4 Cu.sub.3                  1.2     Al.sub.93 W.sub.5 Mn.sub.2                  1     Al.sub.92 Nb.sub.4 Ni.sub.4                  1.5     Al.sub.97 Fe.sub.3                  0.3     Al.sub.92 Fe.sub.5 Co.sub.3                  0.2     Al.sub.96 Fe.sub.1 Ni.sub.3                  0.3     ______________________________________

According to the results of Table 4, Al₉₇ Fe₃, Al₉₂ Fe₅ Co₃ and Al₉₆ Fe₁ Ni₃ wherein the atomic radius difference between Q and M is less than 0.01 Å all have Charpy impact values of less than 1, while Al₉₄ V₄ Mn₂, Al₉₅ Nb₃ Co₂, Al₉₅ Mo₃ Ni₂, Al₉₅ W₄ Cu₁, Al₉₃ V₅ Fe₂, Al₉₅ Nb₃ Cu₂, Al₉₃ V₄ Ni₂, Al₉₃ Mo₄ Cu₃, Al₉₃ W₅ Mn₂ and Al₉₂ Nb₄ Ni₄ wherein the atomic radius difference between Q and M is greater than 0.01 Å all have Charpy impact values greater than 1, which is a level suitable for practical applications.

Although the invention has been described in detail herein with reference to its preferred embodiments and certain described alternatives, it is to be understood that this description is by way of example only, and it is not to be construed in a limiting sense. It is further understood that numerous changes in the details of the embodiments of the invention, and additional embodiments of the invention, will be apparent to, and may be made by persons of ordinary skill in the art having reference to this description. It is contemplated that all such changes and additional embodiments are within the spirit and true scope of the invention as claimed below. 

What is claimed is:
 1. An aluminum-based alloy of high strength and high rigidity consisting essentially of a composition represented by the general formula Al₁₀₀ -(a+b)Q_(a) M_(b) ;wherein Q is at least one metal element selected from the group consisting of V, Mo, Fe, W, Nb, and Pd; M is at least one metal element selected from the group consisting of Mn, Fe, Co, Ni, and Cu; and a and b, which represent a composition ratio in atomic percentages, satisfy the relationships 1≦a≦8, 0<b<5, and 3≦a+b≦8; said aluminum-based alloy having a metallographic structure comprising a quasi-crystalline phase, wherein the difference in the atomic radii between Q and M exceeds 0.01 Å, and said alloy does not contain rare earths.
 2. An aluminum-based alloy of high strength and high rigidity according to claim 1, wherein said metallographic structure is a multiphase structure comprising a quasi-crystalline phase and an aluminum phase.
 3. An aluminum-based alloy of high strength and high rigidity according to claim 1, wherein said metallographic structure is a multiphase structure comprising a quasi-crystalline phase and a metal solid solution having an aluminum matrix.
 4. An aluminum-based alloy of high strength and high rigidity according to claim 1, wherein said metallographic structure is a multiphase structure comprising a quasi-crystalline phase and a stable or metastable intermetallic compound phase.
 5. An aluminum-based alloy of high strength and high rigidity according to claim 1, wherein said metallographic structure is a multiphase structure comprising a quasi-crystalline phase, an amorphous phase, and a metal solid solution having an aluminum matrix.
 6. An aluminum-based alloy of high strength and high rigidity according to claim 1, wherein a+b is not more than
 6. 7. An aluminum-based alloy of high strength and high rigidity according to claim 1, wherein a is not less than
 2. 8. An aluminum-based alloy of high strength and high rigidity according to claim 1, wherein a is not more than
 6. 9. An aluminum-based alloy of high strength and high rigidity according to claim 1, wherein b is not less than
 1. 10. An aluminum-based alloy of high strength and high rigidity according to claim 1, wherein b is not more than
 3. 11. An aluminum-based alloy of high strength and high rigidity according to claim 1, wherein b is not more than
 2. 